I have cast .935 Pro Casting Grain, .935 Regular Casting Grain & .935 Scrap sheet & wire left over from the semester. Here are the results. The raw castings show the most difference as the Pro is the whitest. The Pro casting grain is definitely whiter directly from the flask.

After pickling, you can see a slight difference in color between the three. After wire brushing and polishing, it is very difficult to tell the difference. I cleaned, polished and prepared to granulate on the castings.

I then granulated on each with equally successful results. I first coated each with yellow flux, added the granules, then fused on a charcoal block as usual. There seemed to be no difference.

The liver of sulfur patina was very slow to blacken the Pro. The 935 darkened rapidly and immediately turned black. The scrap was a bit slower and went through stages of golden colors before turning black. The Pro took over twice as long to achieve the dark black as the other two did.

Results were pleasing as I continue to use ALL of the scrap I have as long as I have not soldered. I have previously hammered and formed scrap from an ingot cast into a charcoal block and had very successful results.

 

 

Casting left to right: .935 Pro, .935 regular casting Grain & Scrap .935 Sheet & Wire

 

Pickled in Citric Acid- Pro, 935, Scrap

 

Wire brushed – Pro, 935, Scrap

 

Polished with Tripoli and Rouge- Pro, 935, Scrap

 

Liver of Sulfur Patina – Pro, 935, Scrap

 

Polished after Patina- Pro, 935, Scrap

 

 